Standard Test Method for Ignition Loss of Cured Reinforced Resins

Importancia y uso:

5.1 This test method is used to obtain the ignition loss of a cured reinforced resin sample.

Note 2: The basic concept of burning off of the organic matrix of a reinforced polymer composite has also been shown to be a useful method for enabling a visual examination of the fiber architecture or laminate structure of some reinforcements.

5.2 If only glass fabric or filament is used as the reinforcement of an organic resin that is completely decomposed to volatile materials under the conditions of this test and the small amount of volatiles (water, residual solvent) that are potentially present are ignored, the ignition loss shall be considered to be the resin content of the sample.

5.2.1 This test method does not provide a measure of resin content for samples containing reinforcing materials that lose weight under the conditions of the test or containing resins or fillers that do not decompose to volatile materials released by ignition.

Subcomité:

D20.18

Referida por:

D8505_D8505M-25, D7332_D7332M-23, D3410_D3410M-16R24, D7745-19, D7957_D7957M-25, D2344_D2344M-22, D3262-25, C0582-23, D4203-25, D5630-22, C0364_C0364M-16R24, D8444_D8444M-24, D6416_D6416M-16R24, D7078_D7078M-20R25, D5528_D5528M-21, D6484_D6484M-23, D6041-23, C0273_C0273M-20, D7264_D7264M-21, C0613-23, D5450_D5450M-22, F1173-01R23, C0581-20, E1556-20, D3489-23, D7905_D7905M-19E01, D8131_D8131M-23, D7291_D7291M-22, D3517-24, D5449_D5449M-22, D3935-21, D4101-24, D6115-97R19, D4097-19, D5448_D5448M-22, D5379_D5379M-19E01, D5467_D5467M-97R25, D6783-05AR22, F0790-23, D5630-22, D3753-20, D5766_D5766M-23, C0297_C0297M-16R24, D3039_D3039M-17R25, D3299-24, D2734-23, D5364-14R24, D8101_D8101M-24, D6415_D6415M-22, D5961_D5961M-23, D4762-23, D3982-21, D5229_D5229M-20, D3754-24, D4000-23, D8510_D8510M-23, D7136_D7136M-25, D7248_D7248M-23, D8387_D8387M-23, D5630-22

Volúmen:

08.01

Número ICS:

83.080.10 (Thermosetting materials)

Palabras clave:

fiber architecture; ignition loss; organic matrix; plastics; reinforced polymer composite; reinforced resins; resin content; test method; weight percent;