Standard Test Method for Bursting Strength of Fabrics Constant-Rate-of-Extension (CRE) Ball Burst Test

Importancia y uso:

5.1 This method is used to determine the force required to rupture textile fabric by forcing a steel ball through the fabric with a constant-rate-of-extension tensile tester.

5.2 This is a new method and therefore the history of data is very small, however the agreement of within- laboratory data suggest this method may be considered for acceptance testing of commercial shipments with caution.

5.2.1 If there are differences of practical significance between reported test results for two laboratories (or more), comparative test should be performed to determine if there is a statistical bias between them, using competent statistical assistance. As a minimum, samples used for such comparative test should be as homogeneous as possible, drawn from the same lot of material as the samples that resulted in disparate results during initial testing, and randomly assigned in equal numbers to each laboratory. Other fabrics with established test values may also be used for these comparative tests. The test results from the laboratories involved should be compared using a statistical test for unpaired data, at a probability level chosen prior to the testing series. If bias is found, either its cause must be found and corrected, or future test results for that fabric must be adjusted in consideration of the known bias.

Subcomité:

D13.59

Referida por:

D3787-16R20, D4769-12R24, D5433-12R24, D3786_D3786M-18R23, D7268-23, F3510-21, D4850-23, D3996-23, D3995-23, D5432-12R19, D5378-12R24, D3787-16R20, D3786_D3786M-18R23, F3354-19

Volúmen:

07.02

Palabras clave:

ball burst; bursting strength;