Standard Guide for Testing Polymer Matrix Composite Materials

Importancia y uso:

4.1 This guide is intended to aid in the selection of standards for polymer matrix composite materials. It specifically summarizes the application of standards from ASTM Committee D30 on Composite Materials that apply to continuous-fiber reinforced polymer matrix composite materials. For reference and comparison, many commonly used or applicable ASTM standards from other ASTM Committees are also included.

Subcomité:

D30.01

Referida por:

D8069-17A, D8509_D8509M-23, E2533-21

Volúmen:

15.03

Número ICS:

83.140.20 (Laminated sheets)

Palabras clave:

bearing strength; bearing-bypass interaction; buckling; coefficient of thermal expansion; compaction; composite materials; composites; compression; compressive strength; constituent content; crack-growth testing; creep; creep strength; crippling; CTE; curved-beam strength; damage; damage resistance; damage tolerance; data recording; data records; delamination; density; drop-weight impact; elastic modulus; fastener pull-through; fatigue; fiber; fiber volume; filament; filled-hole compression strength; filled-hole tensile strength; flatwise tensile strength; flexural modulus; flexure; fracture; fracture toughness; gel time; glass transition temperature; hoop-wound; impact; impact strength; lamina; laminate; matrix content; mixed mode; mode I; mode II; mode III; modulus of elasticity; moisture content; moisture diffusivity; OHC; OHT; open-hole compressive strength; open-hole tensile strength; out-of-plane compressive strength; out-of-plane shear strength; out-of-plane tensile strength; panel; peel; penetration resistance; permeability; plate; Poisson's ratio; polymer matrix composites; prepreg; reinforcement; reinforcement content; reinforcement volume; resin; resin content; sandwich construction; shear; shear modulus; shear strength; short-beam strength; specific heat; stepped joint; strain energy release rate; strength; structure; tack; tapered joint; tensile strength; tension; thermal conductivity; thermal diffusivity; thermal expansion coefficient; tow; V-notched beam strength; void content; winding; yarn;