Standard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials

Importancia y uso:

5.1 This test method is designed to yield tensile fatigue data for material specifications, research and development, quality assurance, and structural design and analysis. The primary test result is the fatigue life of the test specimen under a specific loading and environmental condition. Replicate tests may be used to obtain a distribution of fatigue life for specific material types, laminate stacking sequences, environments, and loading conditions. Guidance in statistical analysis of fatigue life data, such as determination of linearized stress life (S-N) or strain-life (ε-N) curves, can be found in Practice E739.

5.2 This test method can be utilized in the study of fatigue damage in a polymer matrix composite such as the occurrence of microscopic cracks, fiber fractures, or delaminations.3 The specimen's residual strength or stiffness, or both, may change due to these damage mechanisms. The loss in stiffness may be quantified by discontinuing cyclic loading at selected cycle intervals to obtain the quasi-static axial stress-strain curve using modulus determination procedures found in Test Method D3039/D3039M. The loss in strength associated with fatigue damage may be determined by discontinuing cyclic loading to obtain the static strength using Test Method D3039/D3039M.

Note 1: This test method may be used as a guide to conduct tension-tension variable amplitude loading. This information can be useful in the understanding of fatigue behavior of composite structures under spectrum loading conditions, but is not covered in this test method.

Subcomité:

D30.04

Referida por:

C1360-17, D7774-22, D6856_D6856M-23, D7791-22, C1358-18, D4762-23

Volúmen:

15.03

Número ICS:

83.140.20 (Laminated sheets)

Palabras clave:

composite materials; fatigue; polymer matrix composites; properties ;