Standard Test Method for Mercurous Nitrate Test for Copper Alloys

Importancia y uso:

5.1 This test method is an accelerated test for detecting the presence of residual (internal) stresses that might result in failure of individual parts in storage or in service due to stress corrosion cracking.

5.2 This test method is not intended for use on assemblies or parts under applied stress. If used for that purpose, the results shall be for information only and not a cause for rejection of the assembly, its component parts, or the original mill product.

Subcomité:

B05.06

Referida por:

B0043-20, B0251_B0251M-17, F0467-13R18, B0150_B0150M-19, B0552-19, F3042-13R24, B0587-19, B0950-23, B0019-20, F0467M-06AR18, B0858-06R24, F0468M-06R18, B0021_B0021M-20, F0468-23, B0138_B0138M-11R24, B0019-20, B0019-20, B0371_B0371M-19, F1387-23, B0111_B0111M-24, B1014-20, B0543_B0543M-18, B0249_B0249M-23, B0956-19E01, B0395_B0395M-18, B0111_B0111M-24, B0359_B0359M-23, B0135_B0135M-17

Volúmen:

02.01

Número ICS:

77.120.30 (Copper and copper alloys)

Palabras clave:

mercurous nitrate; residual stresses; residual stress test; stress corrosion;