Standard Test Method for Tear Resistance (Graves Tear) of Plastic Film and Sheeting

Importancia y uso:

5.1 Tear resistance of plastic film or sheeting is a complex function of its ultimate resistance to rupture. The specimen geometry and speed of testing in this test method are controlled to produce tearing in a small area of stress concentration at rates far below those usually encountered in service. Experience has shown the test to have its best reliability for materials which do not have brittle failure or do not elongate greater than two hundred percent during testing.

5.2 The data from this test method furnish comparative information for ranking the tearing resistance of plastic specimens of similar composition. Actual use performance in tearing of some plastics may not necessarily correlate with data from this test method.

5.3 The resistance to tear of plastic film and sheeting, while partly dependent upon thickness, has no simple correlation with specimen thickness. Hence, tearing forces measured in newtons (or pounds-force) cannot be normalized over a wide range of specimen thickness without producing misleading data as to the actual tearing resistance of the material. Data from this test method are comparable only from specimens, which vary by no more than ±10 % from the nominal or average thickness of all specimens tested. Therefore, the tearing resistance is expressed in maximum newtons (or pounds-force) of force to tear the specimen.

5.4 The tear resistance of plastic film may be a specification that requires the use of this test method, but with some procedural modifications that take precedence when adhering to the specification. Therefore, it is advisable to refer to that material specification before using this test method. Table 1 of Classification System D4000 lists the ASTM materials standards that currently exist.

Subcomité:

D20.19

Referida por:

D7613-17R23, D3105-17R24, D1922-23, D4434_D4434M-21, D8065_D8065M-16R23, D6434-12R18, D5747_D5747M-21, F1742-03R20, D1922-23, D5047-17R23, D7008-08R22, D4551-22, D1922-23, D7176-22, F0942-18R23E01, D7106_D7106M-05R23, D2103-23A, D1593-22, D4068-17R22, F0790-23, F0561-19

Volúmen:

08.01

Número ICS:

83.140.10 (Films and sheets)

Palabras clave:

Graves; plastic film; tear; tear initiation; thin sheeting;